Marglass NT1300
- Composition : > 98% E-Glass
- Weight : 1300 g/m²
- Fiber Diameter : 7-18μm
- Thickness : 10mm
- Density : 130 kg/m³
- Continuous Use Temperature: 500°C
- Instant Temperature Resistance: 1300°C
- Limited Flame Spread: ISO 15025: A1-A2
- Convective Heat : ISO 9151: B2
- Radiant Heat : ISO 6942: C3
- Flame Reaction : NF P 92 503: M1 Class
Marglass NT3300
- Composition : 98% E-Glass
- Weight : 3300 g/m²
- Fiber Diameter : 7-18μm
- Thickness : 25mm
- Density : 130 kg/m³
- Continuous Use Temperature : 500°C
- Instant Temperature Resistance: 1300°C
- Limited Flame Spread: ISO 15025: A1-A2
- Convective Heat : ISO 9151: B2
- Radiant Heat : ISO 6942: C4
- Flame Reaction : NF P 92 503: M1 Class
Preox NT200
- Composition : 100% PAN
- Weight : 200 g/m²
- Thickness : 2mm
- Continuous Use Temperature : 300°C
- Instant Temperature Resistance: 500°C
- Limited Flame Spread: ISO 15025: A1-A2
- Convective Heat : ISO 9151: B1
- Radiant Heat : ISO 6942: C2
- Burn Rate : ISO 3795: 0
- Flame Reaction : NF P 92 503: M1 Class
- Smoke Class : NF F 16-101: F2 Class
Preox NT500
- Composition : 100% PAN
- Weight : 500 g/m²
- Thickness : 4mm
- Continuous Use Temperature : 300°C
- Instant Temperature Resistance: 500°C
- Limited Flame Spread : ISO 15025: A1-A2
- Convective Heat : ISO 9151: B1
- Radiant Heat : ISO 6942: C2
- Burning Rate: ISO 3795: 0
- Flame Reaction : NF P 92 503: M1 Class
- Smoke Class : NF F 16-101: F2 Class